Multistep impregnation method for incorporation of high amount of titania into SBA-15
Wei Wang, Mo Song
Teesside University
Research output
:
Contribution to journal
›
Article
›
peer-review
Overview
Fingerprint
Fingerprint
Dive into the research topics of 'Multistep impregnation method for incorporation of high amount of titania into SBA-15'. Together they form a unique fingerprint.
Sort by
Weight
Alphabetically
Keyphrases
Activity Test
20%
Blockage
40%
Estrogen
20%
High Dispersion
20%
Impregnation Method
100%
Low Angle
20%
Mesochannel
20%
Mesopore
20%
Mesoporous Silica SBA-15
40%
Mesostructure
40%
N2 Adsorption
20%
Nanodomains
20%
No Damage
20%
One-step Impregnation
40%
Photoactivity
20%
Raman Spectra
20%
SBA-15
100%
Sorption Measurements
20%
Titanium Content
20%
Titanium Particles
20%
Transmission Electron Microscopy
20%
UV-DRS
20%
X-ray Powder Diffraction
20%
Physics
Powder X-Ray Diffraction
100%
Raman Spectra
100%
Transmission Electron Microscopy
100%
Volume
100%
Material Science
Diffuse Reflectance Spectroscopy
16%
Silicon Dioxide
33%
Titanium Dioxide
100%
Transmission Electron Microscopy
16%
X Ray Powder Diffraction
16%
Chemical Engineering
Mesopore
100%
Engineering
Raman Spectra
50%